PETG CF: Balance and Performance
PETG CF combines the printability of PETG with the stiffness of carbon fiber. It enables the production of lightweight, strong, and dimensionally stable technical parts for a wide range of industrial applications.
| Standard lead time | About 4 working days, depending on part size, quantity, number of components and finishing degrees. |
|---|---|
| Standard accuracy | ±0.012 in (± 0.3 mm) - may vary depending on geometry. |
| Layer thickness | 0.004 in (0.1 mm) to 0,024 in (0.6 mm) |
| Minimum wall thickness | 0.039 in - 1 mm |
| Maximum build dimensions | Dimensions are unlimited as components may be composed of several sub-parts. The maximum build envelope is 3.28 x 3.28 x 3.28 ft (1000 x 1000 x 1000 mm). |
| Surface structure | Unfinished parts typically have a rough surface but all kinds of fine finishes are possible. FDM/FFF parts can be smoothed, painted and coated. |
| Measure | Value | Test method |
|---|---|---|
| Tensile strength | 7 975 psi | 55 MPa | ASTM D638 |
| Tensile modulus | 945 250 psi | 6 517 MPa | ASTM D638 |
| Elongation at break | 1% | ASTM D638 |
| Heat deflection temperature (HDT) at 66 psi | 171 °F | 77 °C | ISO 75 |
| Density | 1.34 g/cm3 | ISO 1183 |